Mingcheng Group Limited >> Two Component Room Temperature Liquid Silicone Rubber for Mold Making

Two Component Room Temperature Liquid Silicone Rubber for Mold Making

Two Component Room Temperature Liquid Silicone Rubber for Mold Making
Price: US $ 5.7kg
Trade Terms: FOB,CFR,EXW
Min Order: 200kg
Pay Type: L/C,T/T,D/P,Western Union,Paypal
Prod Model: Mcsil-L30
Markets: North America,South America,Eastern Europe,Southeast Asia,Africa,Oceania,Mid East,Eastern Asia,Western Europe
Item: Mcsil-L30
Color: off-White
Mixing Ratio: 100:5
Mixed Viscosity: 16700 Cps
Working Time: 60-80 Mins
Curing Time: 8-12 Hours
Hardness: 28-30 Shore a
Tear Strength: 28 N/Mm
Tensile Strength: 4 MPa
Elongation At Break: 510%
Material: Silicone Rubber
Raw Material: Silicone Raw Material
Appearance: Liquid

Product Description

Description

RTV2 Tin-based silicones, also called condensation cure silicone, are two- component materials which can cure at room temperature to flexible, high tear-strength rubbers. Tin cured silicone can be poured onto models or they can be made brushed by adding a thixotropic additive. They are ideal for molds where easy release or high temperature resistance (Max 200 C) is required.

Characteristics 

Tin cure silicone rubber for molding is white or translucent flowing liquid with general hardness of 15-60shore A after curing. Molding silicone rubber is a kind elastic silicone rubber mold which features with resistance to deformation, high-temperature, acid-alkali and expansion as well as high reproduction times, good tensile strength, tear strength and elongation, Stripping the gender is good, Linear shrinkage rate low, Size stability is good.

Applications 

Tin cured silicone can be used for casting polyurethane, epoxy, polyester resin, PU resin, cement, plaster, gypsum, candle, soap, waxes, toys crafts, poly resin crafts, Lighting, plastic toys, stationery gifts, statue, relieve furniture, furniture decorative materials, artificial stone, building decoration material, sculpture, sandstone, low melt alloys/metals, urethane and so on.

Datasheet 

Item MCSIL-L30
Coloroff-white
Curing agentCA30
Mixing ratio100: 5
Mixed viscosity16700 cps
Working time 60-80 mins
Curing time 8-12 Hours
Hardness28-30 Shore A
Tear Strength28 N/mm
Tensile Strength4 Mpa
Shrinkage≤ 0.3%
Relative density 1.1-1.15 g/cm3
Elongation at break510%

Instructions 

1. Make sure the surface of the original is clean and free of loose material.
2. Weight 100 Part A base and 2 parts of CA30 Curing Agent in a clean container.
3. Stir Part A base silicone before use thoroughly, as filler separation may occur upon prolonged storage.
4. Mix Part A and Part B evenly until the CA30 completely dispersed in the base.
5. Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original
6. De-mold after 24 hours, it will improve the replicate times of silicone mold.
Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mix to completely expand and then collapse. After a further 1-2 minutes under vacuum, the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

Packing 

5kg/plastic drum, 25kg/plastic drum, 25kg/steel drum or 200kg/drum

 
ItemMCSIL-L30
Coloroff-white
Curing agentCA30
Mixing ratio100:5
Mixed viscosity16700 cps
Working time 60-80 mins
Curing time 8-12 Hours
Hardness28-30 Shore A
Tear Strength28 N/mm
Tensile Strength4 Mpa
Shrinkage≤0.3%
Relative density 1.1-1.15 g/cm3
Elongation at break510%



 
MC Silicone is dedicated to manufacturing and R&D a wide variety of mold making and casting materials, such as RTV-2 liquid silicone mold rubbers, liquid polyurethane mold rubbers, silicone fluid, electronic potting silicone compound, foams, release agent and so on. These materials can be used for reproduction of any original model to cast PU resin, polyester resin, epoxy resin, concrete, plaster, foam, wax, soap and all the other decorative mouldings.

MC silicone head office, located in USA, is a tripartite joint venture, China- USA- Taiwan. We have two factories in China mainland. One is for production of RTV2 condensation type silicone and polyurethane, another is for producing addition type silicone and other mold materials. The quality of our silicone products brings good reputation for MC SILICONE in Southeast Asia, Europe, USA and Middle East countries.

Welcome to join us, we will serve you the best with our professional technology, excellent sales service and help you save the cost and enlarge yourbusiness.

Send your message to this manufacturer

  • Mingcheng Group Limited

More >

Other Products with This Manufacturers